GOLDS、LUSTRE FOR GLASS & CERAMICS

Gold Paste, platinum paste Paste Gold , Paste Bright Platinum -

Screen print uses : Burns become temperature 620~850 ℃, 800~980 ℃ , Ens 7% Go 11% All sorts of product

Platinum paste - Burns become temperature 650~920 ℃

Glasswork : Burns become temperature 480~600 ℃ , Quick burn become 10 Minute 720 ℃

1. Applied screen print mesh for 125~165 Eye , Glass for 100~120 Eye .

2. Pack have 100g , 250g , 500g Thinner has 1kg And 25kg Two kinds of wrappings .

Gold Water, platinum water Liquid Gold , Liquid Bright Platinum -

Hand draws use : Ceramic - Burns become temperature 640~820 ℃ , Quick burn become 30~40 Minute 920 ℃ , Ens 8% Go 11% All sorts of product .

Lemon gold water - Burns become temperature 620~780 ℃ , Quick burn become 30~40 Minute 850 ℃ , There is go 6% Go 11%

All sorts of product .

Glasswork - Burns become temperature 480~600 ℃ , Quick burn become 30~40 Minute 640 ℃ , Ens 8% Go 11% All sorts of product , Water

Crystal glass can only use 480 ℃ burn become .

Pack have 100g , 250g Two kinds of .

◎ uses on pay attention to item :

Ordinary gold water submit dark brown , But is very deep articles usage time easily see use situation at surface color , Too can handtailor gold water submit red .

. Will use articles had to clean , Especially want complete dry , Just can bestow picture or screen print , Enters oven burn become front too certain want dryness completely .

. Paint brush had to in advance shi penetrated will can get average screen , And uses for special purpose diluent .

. Excessive gold water or jin gao , Will make product burn become behind submit numbness face or burn burned feel .

◎ about burns become with quality's problem :

. Burns become behind product's surface not light and easy rub fall- Burns become Wen spend low

.Burns become behind product's surface though submit liang li de gold but still easily attrition fall- Burns become shi xu chi Wen 20 minute

. Burns become behind product's surface submit liang li de gold , But has chap phenomenon- Burns become Wen spend high , Will debase burn become temperature

. Will burn become behind product surface submit smoke xun appearance become numbness- Maybe because burn become early days exhaust bad or excess thick

. Use front had better a little amount tests ,treat confirm behind, again formal use.

Flashes glaze Luster Colors -

China uses

Screen print uses: Grain color printing paste, amber color printing paste, shallow blue color printing paste

Diluent abouts 5% or under, mesh suggestion uses 120~165 eyes, pack have 1kg, 5kg two kinds of;

Diluent has 1kg, 25kg two kinds of

Hand picture and sprays Shua use: Grain colorful liquid, amber colorful liquid, other colorful liquid

Colored drawihg or patterns diluent use proportion: Hand draws plus 25%, spray Shua plus 90~300%, pack have 25kg

Glass uses

Heat spray: Grain colorful liquid, amber colorful liquid, other colorful liquid

Direct at 800℃ or above red hot glass surface spray fog colorful liquid (can not addition diluent) ,Xu cold behind (Annealing) and then be OK.

Hand picture and sprays Shua use: Grain colorful liquid, amber colorful liquid

Diluent uses proportion ,hand draws plus 25%, spray Shua plus 90~300%, burns become temperature about 480~620℃

Soak use: Grain colorful liquid

This colored drawihg or pattern liquid want use very use diluent ,burns become temperature about 480~620℃

Above wrapping average for 25kg

◎ uses on pay attention to item:

.Sprays Shua pressure about for 0.7~1.1kg/ cm 2 ,leaves nozzle about 15~50cm positions, uses compressed air can not have steam, otherwise if have

Interfuses colored drawihg or pattern time, will make burn finished goods' surface take on white spot

.Burns become temperature range very wide, from 480~850℃, depends on construct thing's material is glass, porcelain, half porcelain, white cloud comes judgement.

.Burns become behind if surface submit grey, but not grain color, then express very little; burns become behind if surface have lime, then express very many.